Preparation of hydrophilic PVDF/PPTA blend membranes by in situ polycondensation and its application in the treatment of landfill leachate

High modulus poly( p -phenylene terephtalamide) (PPTA) reinforced composites are of great scientific interests. But the thermodynamic difference makes the polymer pairs incompatible and endows the composites with inferior physical-chemical properties. In this study, hydrophilic poly(vinylidene fluoride) (PVDF)/poly( p -phenylene terephtalamide) (PPTA) blend membrane with improved hydrophilicity and mechanical strength was prepared through in situ polycondensation of p -phenylene diamine (PPD) and terephthaloyl chloride (TPC) in PVDF solution and subsequent immersion precipitation phase inversion process. The effects of PPTA concentration in polymer dopes on membrane formation process, structure, morphology and performance were systematically investigated. The results showed that thermodynamically, PPTA acted as a demixing enhancer which accelerated the phase inversion process. Dynamically, liquid-liquid phase separation was still in control of membrane formation process especially in the later period, whereas the addition of PPTA mainly promoted the early emergence of the liquid-liquid demixing. The surface hydrophilicity, ant-fouling properties and mechanical strength were significantly improved when PPTA content was 17   wt%. When PPTA content increased to 26   wt%, membrane bursting pressure increased to nearly 0.6   MPa which was 1.5 times higher than that of PVDF membrane. The resultant PVDF/PPTA blend membrane exhibited an improved antifouling property than that of PVDF membrane when applied in the MBR in the treatment of landfill leachate and also showed a relatively high removal rate of chemical oxygen demand (COD) and chrom.