A new hyperbranched star polyether electrolyte with high ionic conductivity

Hyperbranched poly(glycidol) containing hydroxyl groups was firstly synthesized via anionic polymerization and then reacted with 2-bromoisobutyl bromide to form macroinitiator HPG-Br. Finally, a hyperbranched star polymer (HPG-PPEGMA) was successfully prepared by atom transfer radical polymerization (ATRP) of poly(ethylene glycol) methyl ether methacrylate using HPG-Br as macroinitiator. The structures and properties of the obtained polymers were characterized by 1 H NMR, attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), differential scanning calorimetry (DSC), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The ionic conductivity of the polymer electrolytes composed of HPG-PPEGMA and lithium bis(trifluoromethanesulfonimide) (LiTFSI) was investigated via electrochemical impedance spectroscopy. The results showed that the room temperature ionic conductivity of the prepared hyperbranched star polymer electrolytes had a higher ionic conductivity. When [EO]/[Li] was 20, the ionic conductivity of the hyperbranched star polymer electrolyte was up to 1 × 10 −4  Scm −1 at 30 °C. The onset decomposition temperature of the hyperbranched star polyether could reach 374 °C, indicating that the hyperbranched star polymer had a good thermal stability. The XRD results showed that the structure of the hyperbranched star polymer was beneficial to improve the ionic conductivity due to possessing a low degree of crystallinity.