In Situ Controlled Release of rhBMP-2 in Gelatin-Coated 3D Porous Poly(ε-caprolactone) Scaffolds for Homogeneous Bone Tissue Formation

In tissue engineering, incorporation of bone morphogenetic protein-2 (BMP-2) into biomaterial scaffolds is an attractive strategy to stimulate bone repair. However, suboptimal release of BMP-2 remains a great concern, which may cause unfavorable bone formation as well as severe inflammation. In this study, genipin-cross-linked gelatin entrapped with recombinant human BMP-2 (rhBMP-2) was exploited to decorate the interior surface of three-dimensional porous poly(ε-caprolactone) (PCL) scaffolds. With gelatin-coating, PCL scaffolds demonstrated enhanced water uptake and improved compressive moduli. Intriguingly, a unique release profile of rhBMP-2 composed of a transient burst release followed by a sustained release was achieved in coated scaffolds. These coated scaffolds well supported growth and osteogenesis of human mesenchymal stem cells (hMSCs) in vitro, indicating the retaining of rhBMP-2 bioactivity. When hMSCs-seeded scaffolds were implanted subcutaneously in nude mice for 4 weeks, better bone formation was observed in gelatin/rhBMP-2-coated scaffolds. Specifically, the spatial distribution of newly formed bone was more uniform in gelatin-coated scaffolds than in uncoated scaffolds, which displayed preferential bone formation at the periphery. These results collectively demonstrated that gelatin-coating of porous PCL scaffolds is a promising approach for delivering rhBMP-2 to stimulate improved bone regeneration.