Tunable surface wettability and water adhesion of Sb2S3 micro-/nanorod films

Antimony sulfide (Sb 2 S 3 ) films were successfully prepared by spin coating Sb 2 S 3 micro-/nanorods with different sizes on glass slides, which was synthesized via a facile and rapid microwave irradiation method. The prepared Sb 2 S 3 micro-/nanorods and films were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and water contact angle (CA). The as-prepared Sb 2 S 3 films exhibited different surface wettabilities ranging from superhydrophilicity to superhydrophobicity, which was strongly dependent on the diameter of Sb 2 S 3 micro-/nanorod. Sb 2 S 3 film made by nanorods possessed superhydrophobic surface and high water adhesive property. After surface modification with stearic acid, the superhydrophobic surface exhibited an excellent self-cleaning property owing to its low adhesive force. The clarification of three possible states including Wenzel's state, “Gecko” state and Cassie's state for Sb 2 S 3 film surfaces was also proposed to provide a better understanding of interesting surface phenomena on Sb 2 S 3 films.