Assembly and Valence Modulation of Ordered Bimetallic MOFs for Highly Efficient Electrocatalytic Water Oxidation

Metal synergy can enhance the catalytic performance, and a prefabricated solid precursor can guide the ordered embedding, of secondary metal source ions for the rapid synthesis of bimetallic organic frameworks (MM’-MOFs) with a stoichiometric ratio of 1:1. In this paper, Co-MOF-1D containing well-defined binding sites was synthesized by mechanical ball milling, which was used as a template for the induced introduction of Fe ions to successfully assemble the ordered bimetallic Co 1 Fe 1 -MOF-74@2 (where @2 denotes template-directed synthesis of MOF-74). Its electrocatalytic performance is superior to that of the conventional one-step-synthesized Co 1 Fe 1 -MOF-74@1 (where @1 denotes one-step synthesis of MOF-74), and the ratio of the two metal sources, Co and Fe, is close to 1:1. Meanwhile, the iron valence states (Fe II and Fe III ) in Co 1 Fe 1 -MOF-74@2 were further regulated to obtain the electrocatalytic materials Co 1 Fe 1 (II)-MOF-74@2 and Co 1 Fe 1 (III)-MOF-74@2 . The electrochemical performance test results confirm that Co 1 Fe 1 (II)-MOF-74@2 regulated by valence state has a better catalytic performance than Co 1 Fe 1 (III)-MOF-74@2 in the oxygen evolution reaction (OER) process. This phenomenon is related to the gradual increase in the valence state of Fe ions in Co 1 Fe 1 (II)-MOF-74@2 , which promotes the continuous improvement in the performance of the MOF before reaching the optimal steady state and makes the OER performance reach the optimum when the Fe II /Fe III mixed-valence state reaches a certain proportion. This provides a new idea for the directed synthesis and optimization of highly efficient catalysts.