Chitosan toughened epoxy resin by chemical cross-linking: Enabling excellent mechanical properties and corrosion resistance

There is a growing demand for the development of epoxy resin modified with biomaterials, aiming to achieve high toughness. Herein, chitosan crosslinked epoxy resin (CE) was synthesized by diisocyanate as a bridge. With 4,4′-diamino-diphenylmethane (DDM) as the curing agent, thanks to the unique cross-linking structure of the CE resin and the presence of carbamate groups, the cured CE/DDM exhibited superior properties compared to commercially available epoxy resin (E51). The tensile strength of the cured CE-3/DDM reached 90.17 MPa, the elongation at break was 11.2 %, and the critical stress intensity factor (K IC ) measured 1.78 MPa m 1/2 . These values were 21.4 %, 151.6 %, and 81.6 % higher than those of the cured E51/DDM, respectively. It is worth noting that the addition of biomass material chitosan did not reduce the thermal stability of the resin. Additionally, the CE coatings on the metal substrate exhibited exceptional corrosion resistance , as evidenced by higher impedance values in electrochemical impedance spectroscopy (EIS) and polarization voltages in the Tafel curve compared to those of the E51 coating. This study opens up a novel approach to modifying epoxy resin with biomass materials with high toughness and corrosion resistance, without sacrificing other performance.