Construction of self-repairing polyethersulfone membrane with high density hydrophilic microregions by two dimensional restricted channels for enhanced dyes/salts selective separation

Based on the dye/salts separation efficiency and membrane injury caused by serious pollution of dye/salts wastewater, this study constructed a 2D tight ultrafiltration membrane that could both solve the membrane injury problem and improve the dye/salts separation efficiency, the compatibility of good self-healing performance and penetration performance by 2D material magnesium-aluminum Layered double hydroxide (MgAl-LDH). The self-repairing of physical injury was achieved through the swelling effect of AMPS-PAN, this property was proved by permeate flux, the retention performance of salts in dye/salts solution, the comparison of scanning electron microscope (SEM), and the mechanical strength after physical injury. The healing of chemical injury occured through the reaction of C C and polyethersulfone chain breakage, which was confirmed by X-ray photoelectron spectroscopy (XPS), permeate flux, the retention performance of salts in dye/salts solution, and mechanical property. The high separation efficiency of dye/salts was achieved through 2D material MgAl-LDH, which was proved by separation selectivity ɑ. The compatibility of good self-healing performance and penetration performance was obtained by 2D material MgAl-LDH, which was proved by the penetration and self-healing performance. Morever, the membrane illustrated excellent both permeability and dye/sals separation efficiency, just like the permeate flux, the retention performance of sodium sulfate in methyl blue/sodium sulfate solution, the retention performance of Na 2 SO 4 in methyl blue/Na 2 SO 4 solution, the retention rate of methyl blue were 99.1 L/m 2 h, 12.5%, 7.9%, 97.7%, respectively. The results of pollution index and contact angle also proved that the membrane had anti-pollution performance.