Design and Analysis of a Textured Cu-Encapsulated Ni Tube for Low-Reflection Electromagnetic Interference Shielding Material

With the frequent increase and update of electromagnetic interference (EMI) shielding materials, a low-resolution material that can absorb most electromagnetic waves, thereby effectively reducing the secondary pollution, is urgently needed. However, the excellent performance, flexibility, and low cost of these methods are usually incompatible with current reports. To address the above dilemma, we reported a facile solution for fabricating a low-reflection and high-performance EMI shielding composite by means of electroless nickel plating (EP-Ni), electroless copper plating (EP-Cu), annealing, and coating with a polydimethylsiloxane (PDMS) polymer with the structure of a Ni@Cu tube encapsulated with PDMS. The results indicate that the active groups on vegetable wool can act as active sites for the absorption of the Pd catalyst, thereby catalyzing the reduction of Ni2+, Cu2+, and the subsequent deposition on the plant fiber surface. Notably, the Ni@Cu-encapsulated plant fibers decreased during annealing at 100 °C. According to the segregated network and synergistic effect of the porous structure, the as-fabricated EMI shielding material demonstrated high absorption and low reflection, in which the power coefficient of the T value was approximately 0.0001, the R value was about 0.1764 (a decrease of 27.5% compared that of EP-Ni cotton), and the A value was approximately 0.8235.