Influence of Ca(OH)2 modification on the pore structure and properties of porous glass-ceramics stepwise sintered from granite sludge

The utilization of granite sludge offers significant economic and environmental advantages. This study focuses on preparing porous glass-ceramics from Ca(OH) 2 -modified granite sludge through a two-step sintering process comprising dense sintering and high-temperature foaming, with the addition of 1 % SiC powder as a foaming agent. The impact of foaming temperature and Ca(OH) 2 addition on the structure, compressive strength , specific strength , and thermal conductivity of the porous glass-ceramics is examined. Incorporating the Ca(OH) 2 modifier reduces the glass's viscosity and effectively eliminates micropores on the pore walls. The former promotes foaming and increases porosity, while the latter increases the specific strength of porous glass-ceramics. Increasing both the foaming temperature and the Ca(OH) 2 concentration reduces glass viscosity and promotes mineral dissolution, facilitating the foaming process. However, the specific strength of the porous glass-ceramics initially increases before decreasing due to pore coalescence and excessive mineral dissolution. Theoretical evaluations of compressive strength and thermal conductivity indicate that porous glass-ceramics possess a closed-cell pore structure . Porous glass-ceramic made from granite powder containing 3.5 % Ca(OH) 2 and foamed at 1240 °C exhibits an apparent density and porosity of 0.73 g/cm 3 and 67.1 %, respectively. The compressive strength and thermal conductivity are 14.2 MPa and 0.422 W/(m·K) respectively, with a peak specific strength of 19.4 kN·m/kg. This innovative process enables the scalable recycling of granite sludge into energy-saving building materials.