Influence of stearic acid surface modification on flowability and agglomeration of battery grade Li2CO3 powder

This work investigates the flow and agglomeration behaviors of battery grade Li 2 CO 3 powder and the influence of stearic acid surface modification. The degree of agglomeration is directly related to the uniformity of Li 2 CO 3 and its powder mixtures. According to the Chinese National Nonferrous Metal Industry Standard, battery grade Li 2 CO 3 powder has D 50 equal to 3–8 μm which belongs to a micron-sized superfine powder. Therefore, with the extension of storage time, the serious agglomeration phenomenon occurs due to the large specific surface area and rough and irregular powder particles. The Hausner ratio (HR) of the unmodified sample increases from 1.14 to 1.41, and the corresponding flowability is classified as good to poor. Instead, among samples with doping stearic acid, the optimum amount of it is 0.10 wt% which exhibits an extremely stable HR value from 1.14 to 1.16. Meanwhile, after 156 days, the repose angle (AR) obtained for samples without surface modification and using 0.10 wt% stearic acid are calculated to be 49° and 28°, respectively. Based on the values of HR and AR, the flowability of the unmodified sample is poor while the sample modified with 0.10 wt% of stearic acid still maintain excellent powder flow property. Moreover, The LiMn 2 O 4 cathode material synthesized from modified Li 2 CO 3 powder with a stearic acid content of 0.10 wt% exhibits good crystallinity and comparable electrochemical performance to that prepared by commercial Li 2 CO 3 . These results indicate that stearic acid has the potential to be an ideal modifier for battery grade Li 2 CO 3 powder that needs to be kept for a long time.