In-situ formed Ni2Si into lightweight SiC(rGO) nanocomposite PDCs to boost load bearing-microwave absorption integration for complex environments

As contemporary aerospace and radar-detecting technologies evolve, load bearing-microwave absorption integration of thermal protection materials for complex environment requirements are urgent. Well known for low density, good high-temperature resistance and superior tunable dielectric properties, polymer-derived ceramics (PDCs) promisingly meet most needs of high-performance aircraft thermal protection system (TPS). Aimed at promoting practical application, we integrate in-situ formed Ni 2 Si into lightweight SiC(rGO) nanocomposite PDCs via re-pyrolyzing coassembled nano-Ni/SiC(rGO) p /polycarbosilane-vinyltriethoxysilane-graphene oxide (PVG) blends to enhance their mechanical and electromagnetic wave (EMW) absorbing performances. Size effect on phase transition of Ni into Ni 2 Si (as brazing bonding agents) accompanied by volumetric expansion, ingeniously eliminates stretching stress from PVG precursor inward shrinkage for compact framework during re-pyrolysis. In-situ generated Ni/Ni 2 Si/C core-shell nanostructure (similar to nodular cast iron) has good chemical compatibility with β-SiC/SiO x C y /C free (rGO), thereby enables composites improved compactness and toughness. More interestingly, heterogeneous interfaces/defects among Ni, Ni 2 Si, carbon shell, β-SiC and SiO x C y /C free (rGO) matrix, effectively facilitate interfacial/dipole polarization for robust EMW absorption, and lightweight SiC(rGO, Ni 2 Si) Ni=4% nanocomposite PDCs exhibit outstanding fracture toughness of 6.56 MPa·m 1/2 and high compressive strength of 119.25 MPa. Such composite with structure-function integration maintain stable under butane blowtorch at ∼1300 °C, shedding light on a new route to mass-manufacture aerospace vehicle components.