Mesoporous hollow Fe4[Fe(CN)6)]3 hierarchical nanocrystal architecture for advanced sodium-ion batteries

Prussian blue (PB) has been broadly recognized as promising cathode materials for sodium-ion batteries (SIBs) due to its large interstitial space and robust frame structure, whereas their applications are impeded by unsatisfied long-term cyclability and poor rate capability due to its inherent lattice defects. Herein, we report to fabricate the mesoporous hollow Fe 4 (Fe(CN) 6 ) 3 (one kind of PB) hierarchical nanocrystal architecture by the hydrothermal crystallization and HCl etching of the mesoporous precursor Fe 4 [Fe(CN) 6 ] 3 cubic particles, leading to high crystallinity and large specific surface area. The resultant Fe 4 [Fe(CN) 6 ] 3 cathode for SIBs exhibits a good reversibility and cycling stability with a capacity retention of 75.6 % at 0.5 C after 200 cycles as well as superb rate capability featuring a stable discharge specific capacity of 30.2 mAh g −1 at as high as 10 C, demonstrating the fast kinetics and low polarization of electrochemical reaction, which might be ascribed to the unique architecture and high crystallinity. This offers a new route to designing PB cathode of for SIBs with high rate capabilities.