Preparation of Ce-Doped Gd3(Al, Ga)5O12 Nanopowders via Microwave-Assisted Homogenization Precipitation for Transparent Ceramic Scintillators

Ce-doped gadolinium gallium aluminum oxide (Ce: GGAG) precursors were first prepared by the microwave-assisted homogeneous precipitation method (MAHP). Thermal gravity-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), specific surface area analysis (BET) and field emission scanning electron microscopy (FE-SEM) were employed to investigate the crystal structure, phase evolution and morphologies of the Ce: GGAG precursors and powders. The influence of Ga ion concentration in the salt solution on the properties of Ce: GGAG powders was investigated. All the precursors were transformed into single-phase GGAG after being calcined at 950 °C in a furnace for 3 h. Monodispersed Ce: GGAG powders were obtained as the Ga ion concentration was lower than 0.06 mol/L. Single-phase and dense Ce: GGAG ceramics were obtained after sintering at 1600 °C in a flowing oxygen atmosphere for 10 h. Specifically, the Ce: GGAG ceramic reached its maximum density of ~6.68 g/cm3, which was close to its theoretical density of 6.70 g/cm3, and exhibited the highest optical transmittance of 65.2% at 800 nm after hot isostatic pressing sintering (HIP) as the Ga ion concentration was 0.02 mol/L. The decay time and light yield of the GGAG ceramic were 35 ns and 35,000 ± 1250 ph/MeV, respectively, suggesting that Ce: GGAG ceramics prepared using MAHP-synthesized nanopowders are promising for scintillation applications.