Preparation of photothermal alginate/chitosan derivative/CuS@polydopamine composite fibers and application in desalination

A polyelectrolyte system consisting of sodium alginate (SA) and quaternary ammonium chitosan (QAC) blended with polydopamine-coated copper sulfide particles (CuS@PDA) was chosen to investigate the function of CuS@PDA in the uniform binary blending of anionic and cationic polyelectrolytes in detail. A smart composite fiber SA/QAC/CuS@PDA was prepared via a dry-wet spinning technique. With the addition of CuS@PDA (about 4.3 % in fiber), the as-prepared SA/QAC/ [email protected] fibers ( [email protected] SCFs) showed notably enhanced intensity 359.2 MPa, excellent moisture response, and photothermal conversion performance, with the temperature increasing from 25.9 to 80.7 °C as irradiated under a 980 nm infrared lamp at distance 20 cm away for 120 s. The photothermal performance was maintained after 6 lighting on-and-off cycles. The tensile strength decreased ~23.8 % after 4 cycles, then remained fixed. The diameter increases to ~480 % in wet state but decreases to the original size in dry state for 10 cycles. When the fabric with 90 wt% [email protected] SCFs was used as a water evaporator, the water evaporation rate and efficiency were 1.68 kg·m −2 ·h −1 and 102 % under 1 sun irradiation. This work provides a simple and ecofriendly strategy for fabricating photothermal fabrics by designing and preparing composite fibers.