Synthesis of Ti3C2Tx-MXene/PAN-derived double-loss Co/CeO2/TiO2/CNFs nanocomposites for enhanced microwave absorption performance

With the advancement of wireless communication and electronic equipment , microwave absorption materials (MAMs) have more and more broad applications in related fields. Ti 3 C 2 T x -MXene with unique two-dimensional structure and excellent dielectric properties is often used as a precursor of nano-TiO 2 , which is a potential MAMs. Carbon nanofibers , as a one-dimensional material, have great electrical conductivity and can form interconnected three-dimensional conductive networks. In this study, Ti 3 C 2 T x -MXene was prepared by in-situ HF etching method, and further combined with the benefits of Co, Ce metals, and carbon nanofibers. Co/CeO 2 /TiO 2 /CNFs were prepared via a facile technique for electromagnetic microwave (EM) absorption, exhibiting excellent EM absorption performance due to the synergistic effects of dielectric and magnetic properties . The minimum reflection loss (RL min ) and effective absorption bandwidth (EAB) reache −63.35 dB (11.2 GHz) and 3.6 GHz (9.5–13.1 GHz), with a thickness of only 2.35 mm and a filling rate of 30 wt%, while the maximum EAB reaches 5.4 GHz (12.4–17.8 GHz) with a thickness of 1.82 mm, covering nearly the entire Ku band. By offering a novel strategy to the creation of brand-new, high-performance MAMs based on 1D carbon nanofibers with dielectric/magnetic synergy, this work is believed to support the development of upcoming MAMs.