The structural evolution and electric field-induced strain performance of Bi0.5(Na0.41K0.09)TiO3–Ba(Fe0.5Sb0.5)O3 lead-free piezoelectric ceramics

In recent years, lead-free Bi 0.5 Na 0.5 TiO 3 (BNT) based piezoelectric ceramics with excellent strain properties have gained widespread recognition for their application in high-precision displacement actuators. The (1- x )(0.82Bi 0.5 Na 0.5 TiO 3 -0.18K 0.5 Bi 0.5 TiO 3 )- x Ba(Fe 0.5 Sb 0.5 )O 3 ceramics were fabricated through the die-pressing method in this work. The effect of BFS introduction on the dielectric, ferroelectric and microstructure characteristics of BNKT ceramics was systematically investigated. Among these compositions, the BNKT-0.015BFS ceramics exhibited a piezoelectric strain coefficient ( d 33 *) of 658 pm/V at an electric field of 55 kV/cm, while achieving a strain response of 0.51 % at 85 kV/cm. The observed improvement in strain performance can be attributed to the evolution from non-ergodic relaxor state to ergodic relaxor state caused by BFS substitution. Furthermore, transmission electron microscopy (TEM) explicitly confirmed coexistence of rhombohedral and tetragonal phase and revealed the morphology of nanosized domains. This study adds to a deeper comprehension of the characteristics of strain response enhancement in BNT-based ceramics, opening up avenues for designing novel lead-free piezoelectric ceramics with outstanding electromechanical performance.