Triarylamine-based polyimide COFs for achieving high performance ambipolar multi-color electrochromic energy-storage films

Electrochromic energy storage materials that possess both electrochromic and electrochemical energy-storage properties have attracted significant attention for applications in visual energy-storage, energy-efficient windows, as well as displays. To fulfill their comprehensive applications, electrochromic energy-storage materials require specific characteristics, such as transparency, ambipolarity, multi-color capabilities, and high capacitance. Here, the polyimide covalent-organic framework based on triarylamine (PM-TPI and NT-TPI) COF films were grown successfully on FTO glass through solvothermal polycondensation, and exhibited crystallization, hierarchical porous structures, and ambipolar electrochemical redox activity. Notably, NT-TPI COF film displayed transparent bleached state, ambipolar electrochromism, multi-color (transparent, orange-red, cyan, gray), and high optical contrast. Due to their large specific surface area and efficient electron/ion transport ability, the NT-TPI COF film effectively controlled visible and near-infrared light, achieving optical contrasts of 49.8 % and 70.0 % at 420 and 850 nm, respectively. Moreover, the NT-TPI COF films showed promising electrochemical energy-storage properties and excellent charge–discharge rate performance, with a specific capacitance of 141.0 mAh/g. Additionally, NT-TPI COF/WO 3 -based ambipolar eclectrochromic energy-storage devices also exhibited high optical contrast from visible to near-infrared regions, and large capacitance. In summary, the NT-TPI COF film effectively combines the electrochromic and electrochemical energy-storage capabilities, making it a promising candidate for electrochromic energy-storage materials with transparency, ambipolarity, high optical contrast, multi-color functionality, and high specific capacitance.