The laser damage resistance of optical films holds significant practical importance, as it largely determines both the maximum power output of laser systems and the overall stability of the entire optical assembly. A comprehensive investigation was conducted to examine the influence of both single additives—acetylacetone (ACAC) and diethanolamine (DEA)—and dual-additive systems, specifically ACAC combined with polyethylene glycol 200 (PEG 200) and DEA combined with PEG 200, on TiO2film properties and their laser-induced damage behavior under 1064 nm irradiation. It demonstrated that the films fabricated using ACAC exhibited smoother surfaces. Nevertheless, the sol prepared with DEA was more stable, resulting in films with superior optical properties and an enhanced laser-induced damage threshold (LIDT). The incorporation of dual additives further improved the films’ LIDT. Specifically, the film with DEA and PEG 200 achieved the highest LIDT, reaching 21.5 J/cm2. Moreover, all films exhibited defect-induced damage, yet distinct damage morphologies were observed across different samples. The single-additive films predominantly displayed stress-type damage patterns, whereas the dual-additive films manifested melting-type damage characteristics. Furthermore, through a combination of experiments and calculations, it was revealed that the reasons why the film with DEA and PEG 200 achieved the highest LIDT were twofold: first, the high thermal conductivity of DEA reduced the maximum temperature at the defect center within the film; second, the long molecular chains of PEG 200 created a looser film structure that better mitigated damage caused by stress and expansion during laser irradiation. This study presents a promising approach to enhancing the LIDT through the strategic selection of additives with high thermal conductivity while simultaneously incorporating organic compounds with long molecular chains to develop effective dual-additive films.
危险品化学品经营许可证（带存储）