Selective laser melting and mechanical behavior of Mo-coated diamond particle reinforced metal matrix composites

Defects, such as pores, microcracks, and thermal damage, pose significant challenges in the selective laser melting (SLM) process of diamond reinforced metal matrix composites. To address these issues, this study utilizes Mo-coated diamond particles prepared via salt bath plating for SLM processing of CoCr-diamond composites. The SLM process parameters including laser power, scanning speed, and hatch spacing were systematically optimized using the response surface method (RSM). Subsequently, the microstructure and mechanical properties of the SLMed CoCr-diamond composites were thoroughly investigated. Notably, a protective layer of Mo 2 C is formed on the surface of diamond particles during the salt bath plating process. When compared to the SLMed CoCr-15 vol% Mo-uncoated diamond composite, the Mo coating significantly enhances the compressive strength by 69 % and flexural strength by an impressive 345 % for the CoCr-15 vol% Mo-coated diamond composite.