Grain structure tailoring strategy for heterogeneous lamella SiCp/2024Al composites with exceptional strength-ductility synergy

In this work, a novel grain structure tailoring strategy using one-stepped planetary ball milling , different from conventional powder metallurgy routes that pre-prepared components with different microstructures and then mixed them up, was implemented to fabricate micro- and nano-sized SiC particles (m- & n-SiCp)/2024Al composites with heterogeneous lamella structure. The controllable transformation from homogeneous to heterogeneous grain structures is achieved via nonuniformly distributed n-SiCps induced local grain refinement. Heterogeneous lamella composites exhibit a superior modulus-strength-ductility synergy of 95.3 GPa in Young's modulus , 750.7 MPa in tensile strength and 4.9 % in uniform elongation, particularly with no less than 145 % and 175 % improvements in ductility and toughness, compared with homogeneous composites. Compressive stress relaxation experiments were conducted to reveal the structural dependence of plastic deformation behaviors. Sustainedly rising hetero-deformation induced (HDI) stress produced by extra geometrically necessary dislocation (GND) accumulation at heterogeneous soft/hard domain interfaces and sequential activation of multiple dislocation mediated mechanisms based on load transfer in heterogeneous lamella composites contribute to the enhanced strain hardening capacity, which offers intrinsic toughening . Also, extrinsic toughening originates from enhanced microcrack multiplication and crack-tip blunting.