Novel Aerogel Structure of β-Eucryptite: Featuring Low Density, High Specific Surface Area, and Negative Thermal Expansion Coefficient

Traditional β-eucryptite (LiAlSiO4) is renowned for its unique characteristics of low thermal expansion and high temperature thermal stability, making it an ideal material for precision instruments and aerospace applications. In this study, β-eucryptite was fabricated into an aerogel structure through the sol–gel process and supercritical drying method and using alumina sol as a cost-effective precursor. The synthesized β-eucryptite aerogel demonstrated unique properties including a negative thermal expansion coefficient (−7.85 × 10−6K−1), low density (0.60 g/cm3), and high specific surface area (18.1 m2/g). X-ray diffraction (XRD) and transmission electron microscopy (TEM) mutually corroborated the crystalline structure of β-eucryptite, with XRD confirming the phase purity and TEM imaging revealing well-defined crystal lattice characteristics. Combined nitrogen adsorption–desorption analysis and scanning electron microscopy observations supported the hierarchical porous microstructure, with SEM visualizing interconnected nanoporous networks and nitrogen sorption data verifying the porosity. The negative thermal expansion behavior was directly linked to the β-eucryptite crystal structure, as collectively validated by thermal expansion measurements. Additionally, Fourier transform infrared spectroscopy (FTIR) independently confirmed the aluminosilicate framework structure through characteristic vibrational modes. This research shows the innovation in the synthesis of β-eucryptite aerogel, especially its application potential in precision instruments and building materials that need low thermal expansion and high stability, and the use of aluminum sol as an aluminum source has simplified the preparation steps and reduced production costs.