Rapid Joule-Heating Synthesis of Efficient Low-Crystallinity Ru-Mo Oxide Catalysts for Alkaline Hydrogen Evolution Reaction

Electrocatalytic water splitting has been demonstrated to be a highly efficient and promising technology for green hydrogen production. However, the inefficiency and instability of the cathode hinder its wide application in water electrolysis. Herein, we report a rapid Joule heating method for synthesizing the Ru-Mo oxide catalyst. Comprehensive characterization results confirmed that the as-prepared catalyst featured an internal porous structure with low crystallinity, which weakened the strength of Ru-H bonds through structural and electronic modulation. The enhanced HER performance was attributed to the incorporation of Mo4+species, which strengthened Ru-O-Mo interactions. As tested, the optimized catalyst exhibited ultralow overpotentials (25.08 mV and 120.52 mV @ 10 and 100 mA cm−2, respectively) and excellent stability (100 h @ 100 mA cm−2) in a 1 M KOH solution. Meanwhile, the as-prepared catalyst was equipped in an anion exchange membrane (AEM) alkaline water electrolyzer, which could deliver 185 mA cm−2at only 2.16 V with 100% Faradaic efficiency. This study provides a feasible strategy for constructing highly efficient low-crystallinity electrocatalysts.