Preparation, physicochemical properties and biocompatibility of PBLG/PLGA/bioglass composite scaffolds

In this study, novel poly(γ-benzyl l -glutamate)/poly(lactic- co -glycolic acid)/bioglass (PBLG/PLGA/BG) composite scaffolds with different weight ratios were fabricated using a negative NaCl-templating method. The morphology, compression modulus and degradation kinetics of the scaffolds were characterized. The results showed that the PBLG/PLGA/BG composite scaffolds with a weight ratio of 5:5:1, namely PBLG5PLGA5BG composite scaffolds, displayed a pore size range of 50–500   μm, high compressive modulus (566.6   ±   8.8   kPa), suitable glass transition temperature (46.8   ±   0.2   °C) and low degradation rate (>   8   weeks). The in vitro biocompatibility of the scaffolds was evaluated with MC3T3-E1 cells by live-dead staining, MTT and ALP activity assays. The obtained results indicated that the PBLG5PLGA5BG composite scaffolds were more conducive to the adhesion, proliferation and osteoblastic differentiation of MC3T3-E1 cells than PBLG and PBLG/PLGA composite scaffolds. The in vivo biocompatibility of the scaffolds was evaluated in both SD rat subcutaneous model and rabbit tibia defect model. The results of H&E, Masson's trichrome and CD34 staining assays demonstrated that the PBLG5PLGA5BG composite scaffolds allowed the ingrowth of tissue and microvessels more effectively than PBLG/PLGA composite scaffolds. The results of digital radiography confirmed that the PBLG5PLGA5BG composite scaffolds significantly improved in vivo osteogenesis. Collectively, the PBLG5PLGA5BG composite scaffolds could be a promising candidate for tissue engineering applications.