Preparation and antibacterial activity of Ag/TiO2-functionalized ceramic tiles

An Ag/TiO 2 coating was deposited onto glazed ceramic tiles by a sol-gel and spraying method at high temperatures. The coating was characterized by X-ray diffraction, scanning electron microscopy, and atomic force microscopy . The results showed that silver was present in rutile-TiO 2 , and the temperature did not change the phase composition of the samples. The Ag/TiO 2 coating had a higher roughness than the TiO 2 coating. The tape test (D 3359–08) showed that the coatings prepared at 950 °C and 1000 °C had good adhesion to the ceramic tile substrate. The antibacterial activity of the coating was tested by photocatalytic sterilization experiments. The results showed that the Ag/TiO 2 coating had a higher antibacterial activity than the TiO 2 coating, and the sterilization efficiency of Escherichia coli, Staphylococcus aureus, Shigella , and Salmonella exceeded 99.655% under 2 h of visible light irradiation. This research provides a method to create Ag/TiO 2 coatings with good thermal resistance, adhesion, and antibacterial activity. This improves the low photocatalytic activity caused by the anatase-to-rutile transformation of TiO 2 at high temperatures and the poor adhesion at low temperatures.