Enhancement of PdV/TiO2 catalyst for low temperature DCM catalytic removal and chlorine poisoning resistance by oxygen vacancy construction

TiO 2 -Vo support with abundant oxygen vacancy was prepared by hydrothermal method, purchased TiO 2 -P for comparison, and Pd 0.12 V 4 /TiO 2 catalysts with different TiO 2 structures were prepared to investigate catalytic oxidation for dichloromethane (DCM). Pd 0.12 V 4 /TiO 2 -Vo catalyst showed excellent low temperature DCM removal efficiency, T 90 of which reduced to 290 ℃, and Cl resistance was maintained in 40 h. Abundant oxygen vacancy of TiO 2 -Vo was formed in transformation process of part anatase TiO 2 to rutile phase. The obtained Pd 0.12 V 4 /TiO 2 -Vo catalyst possessed rich acid sites, higher adsorbed oxygen (O ads ) ratio and better oxygen mobility, which inhibited loss of active components and improved DCM removal efficiency. DCM removal efficiency of Pd 0.12 V 4 /TiO 2 catalyst was reduced by HCl, while negative effect in the way of weakening competitive adsorption between HCl and DCM, that would be reduced by TiO 2 supports modification. The present work is favorable for further DCM removal catalyst anti-Cl poisoning modification and application in manufacture industry.