Microstructure and electrical properties of Nb-doped SrTiO3-BiFeO3 based lead-free ceramics

In this work, Nb-doped 0.75SrTiO 3 -0.25BiFeO 3 (ST-BF) lead-free ceramics are designed and synthesized using a conventional solid-state reaction method. The influence of Nb doping on the microstructure, dielectric, and electrical properties are systematically investigated. With the increase of Nb concentration, the crystal structure of ST-BF remains pseudo-cubic as exhibited in the X-ray diffraction patterns. The grain size is found to increase from 0.33 to 6.23 μm, and then decrease to 1.88 μm by Nb doping, along with a clear heterogeneous core–shell microstructure. A relatively low dielectric loss (∼0.1, at 1 kHz) and a stable dielectric constant (∼700, at 1 kHz) are obtained for the 0.03 Nb-doped ST-BF composition at room temperature. Impedance spectroscopy analysis shows that Nb doping in ST-BF increases the total resistivity, forming an electrically conductive core and a nonconductive shell, with enhanced activation energy. The results may provide a feasible approach to develop novel ST-based lead-free dielectric ceramics for capacitor applications.