Molten salt method synthesis of multivalent cobalt and oxygen vacancy modified Nitrogen-doped MXene as highly efficient hydrogen and oxygen Evolution reaction electrocatalysts

Nitrogen-doped Ti 3 C 2 T y MXene with multivalent cobalt and oxygen vacancy (Vo) modification was obtained by using molten salt method and greatly improved electrocatalytic performance. The structural properties of MXene and the valence state of cobalt were adjusted by controlling the molten salt temperature. When the molten salt treatment temperature was 377 °C, the obtained 377-CoO x N 1-x -Ti 3 C 2 T y maintained the chemical structure of MXene well, and also has high Co 2+ content and Vo content. Electrochemical test results showed that 377-CoO x N 1-x -Ti 3 C 2 T y had the lowest Hydrogen Evolution Reaction (HER) overpotential of 87.73 mV and good electrocatalytic stability. X-ray Photoelectron Spectroscopy (XPS) results and Density Functional Theory (DFT) calculations showed that the introduction of polyvalent cobalt and Vo in the nitrogen-doped Ti 3 C 2 T y structure effectively reduced the energy barrier of the electrocatalytic reaction of MXene.