One Step Synthesis of Tetragonal-CuBi2O4/Amorphous-BiFeO3 Heterojunction with Improved Charge Separation and Enhanced Photocatalytic Properties

Tetragonal CuBi2O4/amorphous BiFeO3(T-CBO/A-BFO) composites are prepared via a one-step solvothermal method at mild conditions. The T-CBO/A-BFO composites show expanded visible light absorption, suppressed charge recombination, and consequently improved photocatalytic activity than T-CBO or A-BFO alone. The T-CBO/A-BFO with an optimal T-CBO to A-BFO ratio of 1:1 demonstrates the lowest photoluminescence signal and highest photocatalytic activity. It shows a removal rate of 78.3% for the photodegradation of methylene orange under visible light irradiation for 1 h. XPS test after the cycle test revealed the reduction of Bi3+during the photocatalytic reaction. Moreover, the as prepared T-CBO/A-BFO show fundamentally higher photocatalytic activity than their calcinated counterparts. The one-step synthesis is completed within 30 min and does not require post annealing process, which may be easily applied for the fast and cost-effective preparation of photoactive metal oxide heterojunctions.Keywords:tetragonal CuBi2O4;amorphous BiFeO3;visible light absorption;charge carrier recombination;photocatalytic property