Morphology and Crystal-Plane Effects of Fe/W-CeO2 for Selective Catalytic Reduction of NO with NH3

The CeO2ordinary amorphous, nanopolyhedrons, nanorods, and nanocubes were prefabricated by the hydrothermal method, and employed as carriers of Fe/W–CeO2catalysts to selectively catalyze the reduction of NO with ammonia. Characterization results indicated that the morphology of CeO2support originated from selectively exposing different crystal surfaces, which has a significant effect on oxygen vacancies, acid sites and the dispersion of Fe2O3. The CeO2nanopolyhedrons catalyst (Fe/W–CeO2–P) showed most oxygen vacancies, the largest the quantity of acid sites, the largest BET (Brunauer-Emmett-Teller) surface area and the best dispersion of Fe2O3, which was associated with predominately exposing CeO2(111) planes. Consequently, the Fe/W–CeO2–P catalyst has the highest NO conversion rate in the temperature range of 100–325 °C among the ordinary amorphous, nanorods, and nanocubes Fe/W–CeO2catalysts.Keywords:morphology;Fe/W–CeO2;nanopolyhedra;CeO2(111) planes