Synthesis of Ti6Al4V/SrFHA Composites by Microwave-Assisted Liquid Phase Deposition and Calcination

The feasibility of synthesis of Ti6Al4V/SrFHA (Ca9.37Sr0.63(PO4)6F2) composites via coating strontium and fluorine co-doped HA to Ti6Al4V substrate by microwave-assisted liquid phase deposition and calcination was evaluated, with a focus on the effect of the deposition temperature from 30 °C to 70 °C. The outcomes demonstrate that strontium and fluorine can be successfully doped into HA to form a SrFHA coating with modified micromorphology which is deposited on the alloy. When the deposition temperature was 50 °C, the coating with the largest uniform continuous SrFHA coverage was obtained. After calcination, the adhesion strength and Vickers microhardness of the Ti6Al4V/SrFHA composite increased from 0.68 MPa and 323 HV to 2.41 MPa and 329 HV, respectively, with a decrease in the water contact angle from 10.88° to 7.24°, exhibiting enhancement of both mechanical properties and wettability. Moreover, the composite obtained at the deposition temperature of 50 °C exhibited good bioactivity based on the simulate body fluid (SBF) test. On account of the above features primarily as a result of the combined effect of the co-doping of strontium and fluorine, high crystallinity of SrFHA, large surface roughness, and formation of the titanium oxide transition layer, the Ti6Al4V/SrFHA composite shows great potential in dental implantology.Keywords:microwave processing;liquid phase deposition;co-doping;HA;Ti6Al4V