Preparation and Magnetic Properties of Fe@SiO2 Soft Magnetic Composites

In this work, the insulating SiO2 was coated successfully on the surface of reduced iron particles by a sol-gel method to decrease the core loss at low frequency. The scanning electron microscope images and elements analysis confirm that the surface of iron powders particles were covered by a thin insulating layer in the form of uniform core-shell structure. The samples were annealed at 400 °C in N2 atmosphere to obtain better magnetic properties. The annealed SMCs with 10 mL/h dropping rate of TEOS have optimum magnetic properties with low core loss Ps of 280.89 W/kg and high saturation magnetic flux density Bs of 1.038 T at 1000 Hz.