Effect of La doping on crystalline orientation, microstructure and dielectric properties of PZT thin films

Lanthanum (La)-modified lead zirconate titanate (PLZT) thin films with doping concentration from 0 to 5 at.-% have been fabricated by sol-gel methods to investigate the effects of La doping on crystalline orientation, microstructure and dielectric properties of the modified films. The characterization of PLZT thin films were performed by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and precision impedance analysis. XRD analysis showed that PLZT films with La doping concentration below 4 at.-% exhibited (100) preferred orientation. SEM results indicated that PLZT films presented dense and columnar microstructures when La doping concentration was less than 3 at.-%, while the others showed columnar microstructures only at the bottom of the cross section. The maximum dielectric constant (1502.59 at 100 Hz) was obtained in a 2 at.-% La-doped film, which increased by 53.9 % compared with undoped film. Without introducing a seed layer, (100) oriented PLZT thin films were prepared by using conventional heat treatment process and adjusting La doping concentration.