Effect of polyelectrolyte interlayer on efficiency and stability of p-i-n perovskite solar cells

In this work, we demonstrated a high performance planar heterojunction perovskite solar cell with the polyethylenimine ethoxylated (PEIE) interlayer. By adopting a less polar solvent for PEIE, enhanced device performance and uniformity are achieved. The power conversion efficiency (PCE) of the best device increases by 22% compared to the reference device and reaches 14.82% with J SC of 19.45   mA/cm 2 , V OC of 1.00   V, and FF of 76.31% under AM 1.5G 100   mW/cm 2 light illumination. The UPS measurement shows that the PEIE layer can effectively decrease the energy offset between PCBM and metal electrode. The recombination mechanism was explored by measuring V OC and J SC at various light intensities from 100 to 0.1   mW/cm 2 . It shows that the PEIE layer can suppress the trap-assisted recombination for the devices. The enhancement of the probability of the carriers collection also shows that the recombination is reduced by the PEIE interlayer. Moreover, it is found PEIE layer can improve the stability of the device.