Synthesis and characterization of fluorinated polyurethaneimide electro-optic waveguide material with novel structure

Structurally novel fluorinated polyurethaneimide (PUI) electro-optic polymer based on chromophore molecule b , diisocyanate MDI and anhydride BPAFDA was synthesized by stepwise polymerization of oligomer PUI with fluorinated aromatic diamines BATB and BATPP. Electro-optic (EO) PUI chain structure had the structure of polyimide and polyurethane chain segments, integrating the advantages of polyimide and polyurethane. The PUI possessed good film-forming property, a high glass transition temperature ( T g = 193 °C) and good thermal stability (5 % weight loss temperature T d up to 320 °C). Y-Structured inverted ridge polymer optical waveguides were designed and fabricated using the PUI as the waveguide core material. The PUI had good optical performance with an EO coefficient (γ 33 ) of 79 pm/V and 1.1 dB/cm optical propagation loss at a wavelength of 1550 nm. The results showed that the synthesized PUI met the performance requirements for the preparation of polymer optical waveguide devices and was suitable as a polymer electro-optic waveguide material.