Microstructures and energy storage property of sandwiched BZT-BCT@Fe3O4/polyimide composites

In this paper, the sandwich structured polyimide composite films were studied, in which two layers of pure polyimide films were covered on both sides of BZT-BCT@Fe 3 O 4 /PI composite films. The result indicated that composite films with doped BZT-BCT@Fe 3 O 4 had a significant performance in dielectric properties. The phases and microstructures of BZT-BCT@Fe 3 O 4 and sandwiched composite films were studied by means of XRD, TEM and SEM. It was found that Fe 3 O 4 was present and randomly coated on BZT-BCT. The measured dielectric properties of the composite films show great increased dielectric constant. The dielectric strength of the composite films decreases with the volume fraction raising, however, the relatively high values can be obtained when the fillers content is lower than 5 vol.%. The energy storage density increases significantly at small volume fractions, but decreases significantly at 7 vol.% due to reduced dielectric strength. On the whole, the composite films exhibit higher energy storage density and excellent discharge efficiency when the volume fraction is less than 7%, and the discharge efficiency is still higher than 85% at 265 kV/mm.