Enhanced transduction coefficient in piezoelectric PZT ceramics by mixing powders calcined at different temperatures

Large transduction coefficient ( d 33 × g 33 $d_{33}\times g_{33}$ ) is difficult to obtain in piezoelectric ceramics because these two parameters show opposite trends with compositional modifications. Herein, the Pb(Zr 0.53 Ti 0.47 )O 3 ceramic powders were calcinated under different temperatures (A:830 °C, B:860 °C, and C:890 °C), and then mixed together according to different weight ratios (1A:1B:1C, 1A:2B:1C, 1A:2B:3C and 3A:2B:1C) for ceramics preparation. Both d 33 and g 33 are improved successfully, and the transduction coefficient with the weight ratio of 1A:2B:3C reaches up to 17,500 × 10 −15 m 2 /N, which is 60 % higher than that with the powders calcinated under 830 °C, and at least twice those of commercial PZT-4, PZT-5A and PZT-8 ceramics. The improved transduction coefficient is owing to the enhanced piezoelectric constant and spontaneous polarization resulted from the increased grain size, relative density and the fraction of tetragonal phase. These results indicate that this is a simple but effective way to tailor the transduction coefficient in piezoelectric ceramics .