Chitosan-sodium alginate-based coatings for self-strengthening anticorrosion and antibacterial protection of titanium substrate in artificial saliva

A self-strengthening coating with silver nanoparticles (Ag NPs) doped chitosan (CHI) and sodium alginate (SA) polyelectrolytes was constructed on the surface of polydopamine (PDA) coated Ti substrate by a layer-by-layer assembly method. The PDA coating exhibited an excellent bond with Ti substrate, and also can uniformly deposit Ag NPs via a mild method without introducing any exogenous reductant. The CHI coating was assembled through a spin-coating method for controlling Ag + release. The SA was introduced to enhance the anticorrosion performance by forming calcium alginate (CA) in a corrosive medium. The corrosion protection was investigated with electrochemical impedance spectroscopy and polarization curves tests in fluorine-containing artificial saliva. During immersion, the charge-transfer resistance and the protection efficiency ( ŋ ) presented a continuous increase with the immersion time, demonstrating that this coating possessed a remarkable self-strengthening capability, and the compositions of the outermost film changed from SA to CA with the Ca 2+ cations of the corrosive medium as a crosslinker by SEM and EDS analysis . Furthermore, the ŋ remained up to 96.8% after immersion of 30 days, and then the coating also displayed a distinct inhibition zone on S. mutans . These results prove this coating possesses an excellent anticorrosion performance and antibacterial property .