Effect of ammonium carbonate to metal ions molar ratio on synthesis and sintering of Nd:YAG nanopowders

Using the nanopowders synthesized by a reverse co-precipitation method, neodymium doped yttrium aluminum garnet (Nd:YAG) transparent ceramics were fabricated by vacuum sintering method. The influence of ammonium carbonate to metal ions (NH 4 HCO 3 /M 3+ ) molar ratio (R value) on the properties of Nd:YAG precursors and powders, as well as the densification, microstructure, and transmittance of the resultant ceramics was systematically investigated. The results show that the precursors have similar compositions and the calcined powders have pure Y 3 Al 5 O 12 (YAG) phase. However, the R value is closely related to the morphologies of the precursors and powders. It is found that the powder with R = 3.0 has strongest agglomeration and the powders with R = 3.2–4.0 show better dispersity. Using these powders as starting materials, the corresponding ceramics were sintered at 1720 °C for 20 h in vacuum. As a result, the ceramic with R = 3.2 obtains the best transmittance of about 72% at the wavelength of 1064 nm. The grain growth exponent and activation energy of the Nd:YAG ceramics fabricated from the powder with R = 3.2 were also studied.