MoS2 decorated on one-dimensional MgFe2O4/MgO/C composites for high-performance microwave absorption

Advanced microwave absorption (MA) materials have attracted widespread attention to meet the challenges of electromagnetic (EM) pollution. Herein, MgFe 2 O 4 /MgO/C fibers were successfully prepared via electrospinning technology and carbonization , and their surfaces were coated by MoS 2 via hydrothermal method . The EM wave absorption performance of composites was enhanced due to the introduction of MoS 2 . The results showed that the EM wave absorption performance of MgFe 2 O 4 /MgO/C could not meet the requirements due to low dielectric loss and poor impedance matching. The performance of the composites was improved after coating of MoS 2 , which showed the strong wave absorption capability and the broad absorption bandwidth. The optimal reflection loss (RL) is −56.94 dB at 9.5 GHz and the effective absorption bandwidth is 3.9 GHz (8.08–11.98 GHz) with a thickness of 2.7 mm. The excellent MA performance can be mainly attributed to excellent synergistic effect between MgFe 2 O 4 /MgO/C and MoS 2 . Furthermore, MoS 2 also contributes to dielectric loss and ideal impedance matching. MgFe 2 O 4 /MgO/C@MoS 2 composites may be utilized for lightweight and high-efficient MA materials.