Exploring the effects of cardanol-based co-curing agents with different phosphorus structures on the mechanical and flame-retardant properties of bismaleimide resin

Aiming to address the problems of flammability and brittleness of BMI and reduce the use of petroleum-based materials, three kinds of cardanol-based co-curing agents (CDPO, CDPC, CDCP) were synthesized and applied to prepare advanced BMI . Compared to the neat BMI, the modified BMI exhibited better thermal stability with higher decomposition temperatures and char yields. The BMI/CDCP-10 containing 4.5 wt% CDCP possessed the best flame retardancy with 50.4% reduction in PHRR , 27.5% reduction in THR and 21.2% reduction in TSP compared to those of neat BMI. Moreover, with the 4.5 wt% incorporation of CDPO, CDPC and CDCP, the impact strength of BMI was enhanced by 95%, 133.8% and 127.5% respectively, due to the flexible fatty chains and the decreased crosslinking density . The reason for different modification effects among modified BMI systems is studied from the structure of modifiers, finding that the phosphorylated cardanol with higher content of O and higher valence of P can be utilized to improve the mechanical property and fire safety of BMI. This work provides a new way to reduce the dependence on the petroleum-based materials and expand the application areas of BMI.