Visible-NIR Photodetectors Based on Low-Dimensional GeSe Micro-Crystals: Designed Morphology and Improved Photoresponsivity

Graphical Improved responsivity : GeSe micro-sheets and micro-belts were synthesized by a chemical orientation growth method in 1-octadecene solvent and oleic acid solvent, respectively. The photodetectors based on single micro-belt showed a broadband spectral photoresponse with high responsivity (5562 A/W) and detectivity (3.01×10 12 Jones). It demonstrates significant application potential in the visible and NIR photodetection. GeSe micro-sheets and micro-belts have been synthesized by a facile one-pot wet chemical method in 1-octadecene solvent and oleic acid solvent, respectively. The adsorption of more oleic acid molecules on the (002) plane promoted growth along [010] direction of the GeSe micro-belts and limited carrier transport in this direction, resulting in higher carrier concentration and mobility of the GeSe micro-belts. The performance of the photodetectors based on the single GeSe micro-sheet and the single GeSe micro-belt was investigated under illumination at 532 nm, 980 nm and 1319 nm. Both, photodetectors based on a single GeSe micro-sheet and a single GeSe micro-belt, exhibit a high photoresponse, short response/recovery times, and long-term durability. Moreover, the photodetector based on a single GeSe micro-belt displays a broadband response with a high responsivity (5562 A/W at 532 nm, 1546 A/W at 980 nm) and detectivity (3.01×10 12 Jones at 532 nm, 8.38×10 11 Jones at 980 nm). These excellent characteristics render single GeSe micro-belts very interesting for use as highly efficient photodetectors, especially in the NIR region.