Low-temperature synthesis of high-entropy (Hf0.2Ti0.2Mo0.2Ta0.2Nb0.2)B2 powders combined with theoretical forecast of its elastic and thermal properties

A theoretical calculation combined with experiment was used to study high-entropy (Hf 0.2 Ti 0.2 Mo 0.2 Ta 0.2 Nb 0.2 )B 2 (HEB-HfTiMoTaNb). The theoretical calculation suggested HEB-HfTiMoTaNb could be stable over a wide temperature range. Then, a novel solvothermal/molten salt-assisted borothermal reduction method was proposed to efficiently pre-disperse transitional metal atoms in a precursor and synthesize (Hf 0.2 Ti 0.2 Mo 0.2 Ta 0.2 Nb 0.2 )B 2 nanoscale powders at 1573 K for 6 h, which is nearly 300 K lower than previous reports. The characterization results indicated that the as-synthesized nanoscale HEB-HfTiMoTaNb powder was hexagonal single-phase with homogeneous elements distribution and uniform size, and the oxygen content of the particles is 0.97 wt%. Simultaneously, the mechanical properties, anisotropic nature, and thermal properties of HEB-HfTiMoTaNb were investigated by density functional theory (DFT) calculations. The Cannikin's law was adopted to explain the improvement of comprehensive mechanical properties. In addition, a significant reduction of thermal conductivity was observed for HEB-HfTiMoTaNb and it only was 1/15 of the value of HfB 2 . This work suggests a reliable technique for synthesis of nanosized HEB powders and discovery of high-entropy materials under the guidance of first-principle theory.