Thermally stable broadband near-infrared emitting pyrochlore oxide phosphors codoped with Cr3+ and Yb3+ ions

The advance of portable and smart near-infrared (NIR) light sources has sparked significant interest. However, achieving high-performance NIR emission at longer wavelengths remains a formidable challenge. In this study, we prepared broadband NIR phosphors by codoping pyrochlore oxide Y 2 GaSbO 7 (YGSO) with Cr 3+ and Yb 3+ ions using a conventional high-temperature solid-state reaction. Upon excitation by blue light, YGSO: 0.03Cr 3+ exhibited a broadband NIR emission centered at 765 nm with a full width at half maximum (FWHM) of 160 nm. The purposeful incorporation of Yb 3+ ions facilitated efficient energy transfer from Cr 3+ to Yb 3+ , resulting in a newly observed NIR emission peak at 970 nm. Notably, the addition of Yb 3+ improved the overall thermal quenching resistance owing to its inherent thermal stability. Furthermore, we encapsulated the as-obtained phosphors with commercial blue LED chips to create prototype phosphor-converted light-emitting diodes (pc-LEDs). The Cr 3+ and Cr 3+ -Yb 3+ codoped pc-LEDs achieved output powers of 120 mW@660 mA with a photoelectric conversion efficiency of 12.66%@30 mA, and 131.7 mW@1020 mA with a photoelectric conversion efficiency of 13.93%@30 mA, respectively. These broadband NIR pc-LEDs hold promise for optical imaging applications.