Synthesis of single-phase (ZrTiTaNbMo)C high-entropy carbide powders via magnesiothermic reduction process

Preparation of high-entropy carbides in bulk quantities and in powder form via simple methods at relatively low temperature is challenging. Here, we report the first synthesis of (ZrTiTaNbMo)C high-entropy carbide (HEC) powders via magnesiothermic reduction process. In this, a mixture of individual metallic oxides , graphite and magnesium is treated at a temperature of 1350 °C under Ar atmosphere. The (ZrTiTaNbMo)C powders are obtained after acid leaching, deionized water cleaning and drying process, and synthesized powders shows single-phase face-centered cubic ( fcc ) structure with the oxygen content of only 0.35 wt% and particle-size range of 5–60 µm. Such powders are in potential demand for additive manufacturing techniques, while high dense HEC bulk ceramic is fabricated by hot pressing sintering using ball-milled HEC powders in preliminary researches. The successful synthesis of (ZrTiTaNbMo)C powders may guide the way towards synthesis of many other high-entropy carbide powders via magnesiothermic reduction process.