Medical waste incineration fly ash-based magnesium potassium phosphate cement: Calcium-reinforced chlorine solidification/stabilization mechanism and optimized carbon reduction process strategy

The traditional solidification/stabilization (S/S) technology, Ordinary Portland Cement (OPC), has been widely criticized due to its poor resistance to chloride and significant carbon emissions. Herein, a S/S strategy based on magnesium potassium phosphate cement (MKPC) was developed for the medical waste incineration fly ash (MFA) disposal, which harmonized the chlorine stabilization rate and potential carbon emissions. The in-situ XRD results indicated that the Cl − was efficiently immobilized in the MKPC system with coexisting Ca 2+ by the formation of stable Ca 5 (PO 4 ) 3 Cl through direct precipitation or intermediate transformation (the Cl − immobilization rate was up to 77.29%). Additionally, the MFA-based MKPC also demonstrated a compressive strength of up to 39.6 MPa, along with an immobilization rate exceeding 90% for heavy metals. Notably, despite the deterioration of the aforementioned S/S performances with increasing MFA incorporation, the potential carbon emissions associated with the entire S/S process were significantly reduced. According to the Life Cycle Assessment, the potential carbon emissions decreased to 8.35 × 10 2  kg CO 2 -eq when the MFA reached the blending equilibrium point (17.68 wt.%), while the Cl − immobilization rate still remained above 65%, achieving an acceptable equilibrium. This work proposes a low-carbon preparation strategy for MKPC that realizes chlorine stabilization, which is instructive for the design of S/S materials.