Pb(In1/2Nb1/2)O3-PbZrO3-PbTiO3 ternary ceramics with temperature-insensitive and superior piezoelectric property

The development of ferroelectric ceramics with both large piezoelectric responses and broad service temperature range is still a key challenge for practical applications due to the so-called d 33 - T C trade-off. Here we report the strategy to utilize the synergistic contribution of morphotropic phase boundary and enhanced local structural heterogeneity, in which an excellent piezoelectric coefficient d 33 of 680 pC/N and a high Curie temperature of 330 ℃ are simultaneously achieved in Sm modified 0.25PIN-0.325PZ-0.425PT ceramics. The underlying mechanism responsible for the high dielectric and piezoelectric properties is studied based on cryogenic dielectric measurement and Rayleigh analysis. Of particular interest is that, a high field-induced strain of 0.19% is achieved in 0.25PIN-0.32PZ-0.43PT at electric field of 20 kV/cm, corresponding to a piezoelectric d 33 * of 945 pm/V, showing an excellent temperature stability with minimal variation of 7% up to 310 °C. This work demonstrates the introduction of high temperature end members and rare earth doping are conducive to ferroelectric solid solutions with desired broad usage temperature range and superior piezoelectric properties , which will greatly benefit high temperature actuator applications.