Multifunctional fluorinated ammonium salt for high-performance all-inorganic CsPbI2Br perovskite solar cells with efficiency of 16.29%

All-inorganic CsPbI 2 Br material has attracted considerable attention due to its good balance between phase stability and absorption capacity. However, the power conversion efficiency (PCE) and device stability of CsPbI 2 Br-based perovskite solar cells (PSCs) still lag far behind those of their counterparts, mainly deriving from the notoriously poor moisture stability under humid environment and large serious charge recombination. Herein, a typical phenethylammonium chlorine (PEACl) and its fluorinated derivative 4-fluoro-phenethylammonium chlorine (F-PEACl) are individually incorporated to modify the surface of CsPbI 2 Br film to ameliorate the above issues. Benefiting from the comprehensive passivation effect of ammonium halogen, the trap states of treated CsPbI 2 Br are vastly suppressed. In particular, fluorination significantly increased the dipole moment and hydrophobic property of F-PEACl. Thus, the present CsPbI 2 Br PSC achieves a champion PCE of 16.29% with high open-circuit voltage of 1.272 V, while the reference device and PEACl-treated device yield PCEs of 14.30% and 15.64%, respectively. More importantly, the PSC with F-PEACl capping layer retains 87.2% of its initial PCE after 1000 h storage under 20% RH ambient without encapsulation. Our results reveal the underlying mechanism of performance improvement by surface passivation strategy and provide an effective approach to further boost the CsPbI 2 Br PSC efficiency and stability.