Self-defending mechanism of C/TaC‒SiC composites under 2100°C cyclic ablation environment

To achieve the repeatability of aerospace thermal components, C/TaC‒SiC composites were fabricated. Cycle ablation and bending tests were carried out. After 3 × 60 s of ablation beyond 2100°C, the mechanical property retention rate was 80.9%. Interestingly, a reaction similar to “ouroboros ring,” in which the cyclic reactions of “TaC being oxidized to Ta 2 O 5 and Ta 2 O 5 being reduced to TaC,” occurred in the central ablation region of C/TaC‒SiC composites. On the one hand, the continuous generation of TaC could prevent liquid state Ta 2 O 5 from being blown off central ablation region, playing a similar role in “water and soil conservation.” On the other hand, liquid Ta 2 O 5 covered the surface of C/TaC‒SiC composites during ablation process, contributing to block the inward permeation of oxidized gases. In addition, novel “Grotto” structures were detected in the transitional ablation region of C/TaC‒SiC composites. The formation reason of the “Grotto” structure has also been discussed.