Synthesis and characterization of carbon hollow microspheres

A facile approach was developed for synthesis of carbon hollow microspheres (CHM) via carbonization of the hollow polymer microspheres prepared from polymerization in the presence of l -lysine acted as in situ template. The physical and chemical structures of the samples were investigated by X-ray powder diffraction, Raman spectrum, scanning electron microscopy (SEM), and transmission electron microscopy (TEM). SEM and TEM images show that the products consist of a large scale of monodisperse CHM with a size of about 1.1–1.3 μm. Furthermore, the resulting CHMs possess a surface area of 559 m 2  g −1 and a pore volume of 0.27 cm 3  g −1 . The morphology and the size of the as-obtained samples can be controlled by the polymerization temperature, polymerization time, and the dosage of l -lysine. Moreover, a possible formation mechanism of the CHM has been put forward according to the experimental data available.