Effect of pyrolytic carbon coating on the microstructure and fracture behavior of the Cf/ZrB2-SiC composite

The high sintering temperature and interface interaction seriously degraded the toughening effects of continuous carbon fiber in ZrB 2 -SiC ceramic. The pyrolytic carbon coated carbon fiber reinforced ZrB 2 -SiC composite (C f-PyC /ZrB 2 -SiC) with desirable properties was successfully achieved via brushing nano ZrB 2 -SiC slurry followed by spark plasma sintering at relatively low sintering temperature. The fabricated C f-PyC /ZrB 2 -SiC composite presented a non-brittle fracture feature and a remarkable enhancement in comparison with the ZrB 2 -SiC composite reinforced by the as-received carbon fiber (C f-AS /ZrB 2 -SiC). The fracture toughness and critical crack size were increased from 5.97 ± 0.18–7.66 ± 0.24 MPa m 1/2 and from 91.6 to 164.5 µm, respectively. A high work of fracture of 1915 J/m 2 for C f-PyC /ZrB 2 -SiC composite was achieved, almost four times higher than that of the C f-AS /ZrB 2 -SiC composite (463 J/m 2 ). Multiple toughening mechanisms contributed to such enhancement, such as crack deflection, fiber bridging, fiber pull-out and crack branching. This work provides a feasible approach to fabricate high-performance fiber reinforced ceramic composites having a high work of fracture.